Sensing properties of assembled Bi2S3nanowire arrays
2015
Bismuth sulfide (Bi2S3) nanowires were grown in porous aluminium oxide template and a selective chemical etching was applied to transfer the nanowires to a solution. Well aligned nanowire arrays were assembled on pre-patterned silicon substrates employing dielectrophoresis. Electron beam lithography was used to connect aligned individual nanowires to the common macroelectrode. In order to evaluate the conductometric sensing performance of the Bi2S3 nanowires, current–voltage characteristics were measured at different relative humidity (RH) levels (5–80%) / argon medium. The response of the Bi2S3 nanowires depending of RH is found to be considerably different from those reported for other ty…
Photoelectrochemical characterization of Cu2O-nanowire arrays electrodeposited into anodic alumina membranes
2007
Perfectly aligned nanowire arrays of polycrystalline Cu2O were grown by template-pulsed electrodeposition from a cupric acetate-sodium acetate bath into anodic alumina membranes (AAM). The photoelectrochemical behavior of arrays with different nanowire lengths (0.5 mu m and 2 mu m) was investigated in neutral solution, and the results compared to those pertaining to Cu2O films grown with the same procedure. Although all samples displayed the same indirect bandgap (similar to 1.9 eV), differences were observed both in photocurrent intensity and sign. The latter changed with potential and wavelength in different ways for nanowires and films, revealing a different defect concentration in the t…